R05200 R05400 High Purity TA1 0.5mm Thickness Tantalum Plate TA Sheet Price
Product Parameters
| Item | 99.95% pure R05200 R05400 forged tantalum sheet for sale |
| Purity | 99.95% min |
| Grade | R05200, R05400, R05252, R05255, R05240 |
| Standard | ASTM B708, GB/T 3629 |
| Technique | 1.Hot-rolled/Cold-rolled; 2.Alkaline Cleaning;3.Electrolytic Polish; 4.Machining, grinding; 5.Stress relief annealing |
| Surface | Polished, grinding |
| Customized products | According to drawing, Special requirements to be agreed upon by the supplier and buyer. |
| Feature | high ductility, corrosion resistance, high desity |
| Application | Petroleum, Aerospace, Mechanical, Chemical |
Specification
|
Dimensions |
|||
|
Item |
Thickness/mm |
Width/mm |
Length/mm |
|
Foil |
0.05 |
300 |
>200 |
|
Sheet |
0.1--0.5 |
30- 609.6 |
30-1000 |
|
Plate |
0.5--10 |
50-1000 |
50-2000 |
Mechanical requirements
| Grade and size | Annealed | ||
| Tensile strength min, psi (MPa) | Yield strength min,psi (MPa)(2%) | Elongation min, % (1 inch gage length) | |
| Sheet, foil. and board (RO5200, RO5400) Thickness<0.060"(1.524mm) Thickness≥0.060"(1.524mm) | 30000 (207) | 20000 (138) | 20 |
| 25000 (172) | 15000 (103) | 30 | |
| Ta-10W (RO5255)Sheet, foil. and board | 70000 (482) | 60000 (414) | 15 |
| 70000 (482) | 55000 (379) | 20 | |
| Ta-2.5W (RO5252)Thickness<0.125" (3.175mm)
Thickness≥0.125" (3.175mm) |
40000 (276) | 30000 (207) | 20 |
| 40000 (276) | 22000 (152) | 25 | |
| Ta-40Nb (RO5240)Thickness<0.060"(1.524mm) | 40000 (276) | 20000 (138) | 25 |
| Thickness>0.060"(1.524mm) | 35000 (241) | 15000 (103) | 25 |
Chemical composition
| Chemistry (%) | |||||||||||||
| Designation | Chief component | Impurities maxmium | |||||||||||
| Ta | Nb | Fe | Si | Ni | W | Mo | Ti | Nb | O | C | H | N | |
| Ta1 | Remainder | 0.004 | 0.003 | 0.002 | 0.004 | 0.006 | 0.002 | 0.03 | 0.015 | 0.004 | 0.0015 | 0.002 | |
| Ta2 | Remainder | 0.01 | 0.01 | 0.005 | 0.02 | 0.02 | 0.005 | 0.08 | 0.02 | 0.01 | 0.0015 | 0.01 | |
Features
* Good ductility
* Good plasticity
* Excellent acid-resistance
* High melting point, high boiling point
* Very small coefficients of thermal expansion
* Good capability of absorbing and releasing hydrogen
Application
Tantalum is used to produce various types of alloys with high melting point, strength and malleability.
By alloying with other metals, we can manufacture cemented carbide tools for metal processing, jet engine parts, chemical processing equipment, nuclear reactors, missile parts, heat exchangers, superalloys for tanks and containers, etc. Used for purposes.
Related products
-
Factory Direct Supply High Quality Ruthenium Pe...
Chemical composition and specifications Ruthenium Pellet Main content: Ru 99.95% min (excluding gas element) Impurities(%) Pd Mg Al Si Os Ag Ca Pb <0.0005 <0.0005 <0.0005 <0.0030 <0.0100 <0.0005 <0.0005 <0.0005 Ti V Cr Mn Fe Co Ni Bi <0.0005 <0.0005 <0.0010 <0.0005 <0.0020 <0.0005 <0.0005 <0.0010 Cu Zn As Zr Mo Cd Sn Se <0.0005 <0.0005 <0.0005 <0.0005 <0.00...
-
Hot Selling Best Price 99.95%Min. Purity Molybd...
Product Parameters Item name Hot Selling Best Price 99.95%min. Purity Molybdenum Crucible /Pot for Melting Purity 99.97% Mo Working temperature 1300-1400Centigrade:Mo1 2000 Centigrade:TZM 1700-1900Centigrade: MLa Delivery time 10-15 days Other Material TZM, MHC, MO-W, MO-RE, MO-LA，Mo1 Dimension & Cubage According to your needs or drawings Surface Finish turning, Grinding Density 1.Sintering molybdenum crucible Density: ...
-
Molybdenum Scrap
By far the largest use of molybdenum is as alloying elements in steels. It is therefore mostly recycled in the form of steel scrap.Molybdenum “units” are returned to the surface where they melt together with the primary molybdenum and other raw materials to make steel. The proportion of scrap reused varies by products segments . Molybdenum-containing stainless steels like these type 316 solar water heaters are diligently collected at the ir end-of-life due to their nigh value. In...
-
Customized High Purity 99.95% Wolfram Pure Tung...
Product Parameters Material tungsten Color sintered, sandblasting or polishing Purity 99.95% Tungsten Grade W1,W2,WAL,WLa,WNiFe Product Feature High melting point, High- density, high temperature oxidation resistance, long service life, resistance to corrosion. Property high hardness and strength, excellent corrosion resistance Desity 19.3/cm3 Dimension Customized Standard ASTM B760 Melting point 3410℃ Design&Size OE...
-
Tantalum Sheet Tantalum Cube Tantalum Block
Product Parameters Density 16.7g/cm3 Purity 99.95% Surface bright, without crack Melt point 2996℃ Grain size ≤40um Process sintering,hot rolling, cold rolling ,annealing Application medical,industry Performance Moderate hardness, ductility, high toughness and low coefficient of thermal expansion Specification Thickness(mm) Width(mm) Length(mm) Foil 0.01-0.0...
-