Pure Cobalt Ingots - Niobium Target – HSG Metal
Pure Cobalt Ingots - Niobium Target – HSG Metal Detail:
Product parameters
| Specification | |
| Item | ASTM B393 9995 pure polished niobium target for industry |
| Standard | ASTM B393 |
| Density | 8.57g/cm3 |
| Purity | ≥99.95% |
| Size | according to customer’s drawings |
| Inspection | Chemical composition testing, Mechanical testing, Ultrasonic inspection, Appearance size detection |
| Grade | R04200, R04210, R04251, R04261 |
| Surface | polishing, grinding |
| Technique | sintered, rolled, forged |
| Feature | High temperature resistance, corrosion resistance |
| Application | Superconducting industry, Aerospace aviation, Chmeical Industry, Mechanical |
|
Chemical Composition |
|||
| Grade |
R04200 |
R04210 |
|
| Main element |
Nb |
Bal |
Bal |
| Impurity elements |
Fe |
0.004 |
0.01 |
|
Si |
0.004 |
0.01 |
|
|
Ni |
0.002 |
0.005 |
|
|
W |
0.005 |
0.02 |
|
|
Mo |
0.005 |
0.01 |
|
|
Ti |
0.002 |
0.004 |
|
|
Ta |
0.005 |
0.07 |
|
|
O |
0.012 |
0.015 |
|
|
C |
0.035 |
0.005 |
|
|
H |
0.012 |
0.0015 |
|
|
N |
0.003 |
0.008 |
|
|
Mechanical Property |
|||
|
Grade |
Tensile Strength ≥ Mpa |
Yield Strength ≥ Mpa(0.2% residual deformation) |
Extend Rate % (25.4mm measurement) |
|
R04200 R04210 |
125 |
85 |
25 |
|
Content, Max, Weight % |
||||
|
Element |
Grand: R04200 |
Grand:R04210 |
Grand:R04251 |
Grand:R04261 |
|
Unalloyed Niobium |
Unalloyed Niobium |
(Reactor grade niobium-1% Zirconium) |
(Commercial grade niobium-1% Zirconium) |
|
|
C |
0.01 |
0.01 |
0.01 |
0.01 |
|
O |
0.015 |
0.025 |
0.015 |
0.025 |
|
N |
0.01 |
0.01 |
0.01 |
0.01 |
|
H |
0.0015 |
0.0015 |
0.0015 |
0.0015 |
|
Fe |
0.005 |
0.01 |
0.005 |
0.01 |
|
Mo |
0.01 |
0.02 |
0.01 |
0.05 |
|
Ta |
0.1 |
0.3 |
0.1 |
0.5 |
|
Ni |
0.005 |
0.005 |
0.005 |
0.005 |
|
Si |
0.005 |
0.005 |
0.005 |
0.005 |
|
Ti |
0.02 |
0.03 |
0.02 |
0.03 |
|
W |
0.03 |
0.05 |
0.03 |
0.05 |
|
Zr |
0.02 |
0.02 |
0.8~1.2 |
0.8~1.2 |
|
Nb |
Remainder |
Remainder |
Remainder |
Remainder |
Product technology
The vacuum electron beam melting process produces niobium plates. The unforged niobium bar is first smelted into a niobium ingot through a vacuum electron beam melting furnace. It is usually divided into single smelting and multiple smelting. We usually use twice smelted niobium ingots. Depending on the product requirements, we can perform more than two smelting.
Application
Superconducting industry
Used to produce niobium foil
Heat shield in high temperature furnace
Used to produce niobium welded pipe
Used in the production of human implants.
Product detail pictures:
Related Product Guide:
We purpose to understand high quality disfigurement with the output and supply the top service to domestic and overseas buyers wholeheartedly for Pure Cobalt Ingots - Niobium Target – HSG Metal , The product will supply to all over the world, such as: Romania, Iraq, Swiss, Our company offers the full range from pre-sales to after-sales service, from product development to audit the use of maintenance, based on strong technical strength, superior product performance, reasonable prices and perfect service, we'll continue to develop, to supply the high-quality goods and services, and promote lasting cooperation with our customers, common development and create a better future.
By Ella from Cape Town - 2017.03.28 16:34
Problems can be quickly and effectively resolved, it is worth to be trust and working together.
By Ivy from Greek - 2018.12.11 11:26
Related products
-
Tungsten Scrap For Sale - High Density Customi...
Product Parameters Tungsten Block Polished 1kg Tungsten Cube 38.1mm Purity W≥99.95% Standard ASTM B760, GB-T 3875, ASTM B777 Surface Ground Surface, Machined surface Density 18.5 g/cm3 –19.2 g/cm3 Dimensions Common sizes：12.7*12.7*12.7mm20*20*20mm 25.4*25.4*25.4mm 38.1*38.1*38.1mm Application Ornament, decoration, Balance weight, desktop, gift, target, Military industry, and so on The characteristics 1. Laser engraving tungsten cube for 1kg 2. Melting point ...
-
Molybdenum Scrap - High Quality Price Per Kg M...
Product Parameters Product name Pure molybdenum cube / molybdenum block for industry Grade Mo1 Mo2 TZM Type cube, block, ignot,lump Surface Polish/grinding/chemical wash Density 10.2g/cc Processing Rolling, Forging, Sintering Standard ASTM B 386-2003, GB 3876-2007, GB 3877-2006 Size Thickness: min0.01mmWidth: max 650mm Popular size 10*10*10mm / 20*20*20mm / 46*46*46 mm / 58*58*58mm Chemical requirements Element Ni Mg Fe Pb Al Bi Si Cd Ca P Concentration(%) 0.003 0.0...
-
Tungsten Rectangular Bar - Customized High Pur...
Product Parameters Material tungsten Color sintered, sandblasting or polishing Purity 99.95% Tungsten Grade W1,W2,WAL,WLa,WNiFe Product Feature High melting point, High- density, high temperature oxidation resistance, long service life, resistance to corrosion. Property high hardness and strength, excellent corrosion resistance Desity 19.3/cm3 Dimension Customized Standard ASTM B760 Melting point 3410℃ Design&Size OEM or ODM acceptable Chemical Compositio...
-
9995 Pure Molybdenum Bar Rod - Molybdenum Pric...
Product Parameters Term Molybdenum bar Grade Mo1,Mo2,TZM,Mla,etc Size as request Surface condition hot rolling, cleaning, polishedc MOQ 1 kilograms Test and Quality dimension inspection appearance quality test process performance test mechanical properities test Load port shanghai shenzhen qingdao Packing standard wooden case, carton or as request Payment L/C, D/A, D/P, T/T, Western union, MoneyGram, Paypal, Wire-transfer Delivery time 10-15 working days ...
-
99.995 Indium Ingot - Tantalum Target – ...
Product parameters Product Name：high purity tantalum target pure tantalum target Material Tantalum Purity 99.95%min or 99.99%min Color A shiny, silvery metal that is very resistant to corrosion. Other name Ta target Standard ASTM B 708 Size Dia >10mm * thick >0.1mm Shape Planar MOQ 5pcs Delivery time 7days Used Sputtering Coating Machines Table 1: Chemical composition Chemistry (%) Designation Chief component Impurities maxmium Ta Nb Fe...
-
Ferro Vanadium Uses - Ferro Vanadium – H...
Specification of Ferrovanadium Brand Chemical Compositions (%) V C Si P S Al Mn ≤ FeV40-A 38.0~45.0 0.60 2.0 0.08 0.06 1.5 — FeV40-B 38.0~45.0 0.80 3.0 0.15 0.10 2.0 — FeV50-A 48.0~55.0 0.40 2.0 0.06 0.04 1.5 — FeV50-B 48.0~55.0 0.60 2.5 0.10 0.05 2.0 — FeV60-A 58.0~65.0 0.40 2.0 0.06 0.04 1.5 — FeV60-B 58.0~65.0 0.60 2.5 0.10 0.05 2...