Hot-selling Sintering Molybdenum Bar - 99.95 Molybdenum Pure Molybdenum Product Moly Sheet Moly Plate Moly Foil In High Temperature Furnaces And Associated Equipment – HSG Metal
Hot-selling Sintering Molybdenum Bar - 99.95 Molybdenum Pure Molybdenum Product Moly Sheet Moly Plate Moly Foil In High Temperature Furnaces And Associated Equipment – HSG Metal Detail:
Product Parameters
| Item | molybdenum sheet/plate |
| Grade | Mo1, Mo2 |
| Stock size | 0.2mm, 0.5mm, 1mm, 2mm |
| MOQ | hot rolling, cleaning, polished |
| Stock | 1 kilograms |
| Property | anti-corrosion, high temperature resistance |
| Surface Treatment | Hot-rolled alkaline cleaning surface |
| Electrolytic polish surface | |
| Cold-rolled surface | |
| Machined surface | |
| Technology | extrusion, forging and rolling |
| Test and Quality | dimension inspection |
| appearance quality test | |
| process performance test | |
| mechanical properities test | |
| The specification would be changed by the customers’ requirements. | |
Specification
| Width, mm | Thickness, mm | Thickness deviation, min, mm | Flatness, % | |||
| <300mm | >0.13mm | ±0.025mm | 4% | |||
| ≥300mm | >0.25mm | ±0.06mm | 5%-8% | |||
| Purity(%) | Ag | Ni | P | Cu | Pb | N |
| <0.0001 | <0.0005 | <0.001 | <0.0001 | <0.0001 | <0.002 | |
| Si | Mg | Ca | Sn | Ba | Cd | |
| <0.001 | <0.0001 | <0.001 | <0.0001 | <0.0003 | <0.001 | |
| Na | C | Fe | O | H | Mo | |
| <0.0024 | <0.0033 | <0.0016 | <0.0062 | <0.0006 | >99.97 | |
Specification
| Specifications for molybdenum wire: | ||
| Molybdenum Wire Types | Diameter (inch) | Tolerance (%) |
| Molybdenum Wire for EDM | 0.0024″ ~ 0.01″ | ±3% wt |
| Molybdenum Spray Wire | 1/16″ ~ 1/8″ | ±1% to 3% wt |
| Molybdenum Wire | 0.002″ ~ 0.08″ | ±3% wt |
| Molybdenum Wire(clean) | 0.006″ ~ 0.04″ | ±3% wt |
Specificantions Range
1) Thickness: Hot-rolled plate:1.5~40mm; Cold-rolled plate/sheet:0.05~3.0mm
2) Width: Hot-rolled plate:≤750mm; Cold-rolled plate/sheet: ≤1050mm;
3) Length: Hot-rolled plate:≤3500mm; Cold-rolled plate/sheet: ≤2500mm
Application
| Classification | Feature | Application field |
| Pure Mo plate | High melting point, high purity, low thermal expansivity, excellent thermal conductivity, welding performance and processability | Widely used for manufacturing electron (ion) beam sputtering target, spare parts for ion implantation machine, heat sink of semiconductor, parts of electron tube, MOCVD equipment, and medical device, hot zone, crucible and supporting elements for sapphire crystal furnace, heater, heat shield, supporting element, and boat for vacuum and hydrogen shielded heating furnace |
| Pure Mo plate treated in high temperature | High-purity, consistent in physical and chemical property, and excellent high temperature anti-deforming capability | Suitable for manufacturing base plate for precision electronic ceramics and rear-earth material |
| Lanthanum-doped Mo plate | By using oxide dispersion strengthening mechanism, certain plastic deformation could be performed under room temperature after being treated in high temperature because of its high strength, high recrystallization temperature and excellent high-temperature strength and improved recrystallization brittleness and high temperature anti-deforming capability | particularly suitable for fabricating components used in more than 1500℃ work environment, such as heater, heat shield, base plate and boat for high temperature furnace |
| Lanthanum-doped Mo plate treated in high temperature | Excellent high-temperature strength, and low high temperature deformation due to its oxide dispersion strengthening effect and specific structure | suitable for making base plate for sintering fine ceramics and rear-earth ceramic, bearing rack, base plate and coat for high temperature heating furnace |
| Doped Mo plate | High temperature strength, low recrystallization temperature, and excellent high-temperature creep resistant performance because of its potassium bubble strengthening mechanism | particularly suitable for fabricating products with low high-temperature creep, such as components for electron tube, heater, heat shield, and so on for high temperature furnace |
| Doped Mo plate treated in high temperature | Low high-temperature creep due to its long grain staggered structure and high purity | suitable for making products with high requirement to purity and high-temperature creep, such as base plate for electronic ceramics sintering or heat-treating, supporting elements in electron tube, and so on |
| Cross-rolled pure Mo plate | Low anisotropy and good bending performance | particularly suitable for elongating, spinning, reinforcing and bending, and making elongating or spinning Mo crucible, Mo parts need to reinforce or bend, such as corrugated sheet, bending piece, Mo boat, and so on |
| Cross-rolled pure Mo plate treated in high temperature | Low anisotropy and good bending performance besides same performance of Lanthanum-doped Mo plate | particularly suitable for reinforcing and bending, and making reinforced or bended Mo parts with high temperature requirement, such as heating zone, bended fabricated parts, high-temperature Mo boat, and so on |
Product detail pictures:
Related Product Guide:
That has a positive and progressive attitude to customer's interest, our organization consistently improves our products quality to satisfy the demands of shoppers and further focuses on safety, reliability, environmental specifications, and innovation of Hot-selling Sintering Molybdenum Bar - 99.95 Molybdenum Pure Molybdenum Product Moly Sheet Moly Plate Moly Foil In High Temperature Furnaces And Associated Equipment – HSG Metal , The product will supply to all over the world, such as: United States, Washington, Jamaica, If you give us a list of products you are interested in, along with makes and models, we can send you quotations. Please email us directly. Our goal is to establish long-term and mutually profitable business relationships with domestic and overseas clients. We look forward to receiving your reply soon.
By EliecerJimenez from Montreal - 2017.02.14 13:19
Problems can be quickly and effectively resolved, it is worth to be trust and working together.
By King from Birmingham - 2018.02.21 12:14
Related products
-
2022 wholesale price Ferro-Molybdeen - China F...
Chemical Composition FeMo composition (%) Grade Mo Si S P C Cu FeMo70 65-75 2 0.08 0.05 0.1 0.5 FeMo60-A 60-65 1 0.08 0.04 0.1 0.5 FeMo60-B 60-65 1.5 0.1 0.05 0.1 0.5 FeMo60-C 60-65 2 0.15 0.05 0.15 1 FeMo55-A 55-60 1 0.1 0.08 0.15 0.5 FeMo55-B 55-60 1.5 0.15 0.1 0.2 0.5 Products Description Ferro Molybdenum70 is mainly used to add molybdenum to steel in steel making. Molybde...
-
Sell Indium Ingot - Tantalum Target – HS...
Product parameters Product Name：high purity tantalum target pure tantalum target Material Tantalum Purity 99.95%min or 99.99%min Color A shiny, silvery metal that is very resistant to corrosion. Other name Ta target Standard ASTM B 708 Size Dia >10mm * thick >0.1mm Shape Planar MOQ 5pcs Delivery time 7days Used Sputtering Coating Machines Table 1: Chemical composition Chemistry (%) Designation Chief component Impurities maxmium Ta Nb Fe...
-
Wholesale Price China Ferromolybdenum Fe-Mo - ...
Product Parameters Item name Hot Selling Best Price 99.95%min. Purity Molybdenum Crucible /Pot for Melting Purity 99.97% Mo Working temperature 1300-1400Centigrade:Mo1 2000 Centigrade:TZM 1700-1900Centigrade: MLa Delivery time 10-15 days Other Material TZM, MHC, MO-W, MO-RE, MO-LA，Mo1 Dimension & Cubage According to your needs or drawings Surface Finish turning, Grinding Density 1.Sintering molybdenum crucible Density: >9.8g/cm3; 2.Forging molybdenum crucible D...
-
China wholesale Cobalt Metal Price - high puri...
Product parameters Brand Name HSG Metal Model Number HSG-moly target Grade MO1 Melting point(℃) 2617 Processing Sintering/ Forged Shape Special Shape Parts Material Pure molybdenum Chemical Composition Mo:> =99.95% Certificate ISO9001:2015 Standard ASTM B386 Surface Bright and Ground Surface Density 10.28g/cm3 Color Metallic Luster Purity Mo:> =99.95% Application PVD coating film in glass industry , ion plating Advantage High Temperature Resistance, Hig...
-
Chromium Metal Price - GOOD QUALITY PURE CHROM...
Metal Chromium Lump / Cr Lmup Grade Chemical Composition % Cr Fe Si Al Cu C S P ≧ ≦ HRCR99-A 99 0.30 0.25 0.30 0.01 0.01 0.01 0.01 HRCR99-B 99 0.40 0.30 0.30 0.00 0.02 0.02 0.01 HRCR98.5-A 98.5 0.45 0.35 0.50 0.04 0.03 0.02 0.01 HRCR98.5-B 98.5 0.50 0.40 0.50 0.06 0.03 0.02 0.01 HRCR98 98 0.80 0.40 0.80 0.02 0.05 0.03 0.01 Description Metal chromi...
-
Hot sale Buy Indium Metal Ingot - Tungsten Tar...
Product parameters Product Name Tungsten(W)sputtering target Grade W1 Available Purity(%) 99.5%,99.8%,99.9%,99.95%,99.99% Shape: Plate, round, rotary, pipe/tube Specification As customers demands Standard ASTM B760-07,GB/T 3875-06 Density ≥19.3g/cm3 Melting point 3410°C Atomic volume 9.53 cm3/mol Temperature coefficient of resistance 0.00482 I/℃ Sublimation heat 847.8 kJ/mol(25℃) Latent heat of melting 40.13±6.67kJ/mol State Planar tungsten target,Rotating tung...