Hot-selling Sintering Molybdenum Bar - 99.95 Molybdenum Pure Molybdenum Product Moly Sheet Moly Plate Moly Foil In High Temperature Furnaces And Associated Equipment – HSG Metal
Hot-selling Sintering Molybdenum Bar - 99.95 Molybdenum Pure Molybdenum Product Moly Sheet Moly Plate Moly Foil In High Temperature Furnaces And Associated Equipment – HSG Metal Detail:
Product Parameters
| Item | molybdenum sheet/plate |
| Grade | Mo1, Mo2 |
| Stock size | 0.2mm, 0.5mm, 1mm, 2mm |
| MOQ | hot rolling, cleaning, polished |
| Stock | 1 kilograms |
| Property | anti-corrosion, high temperature resistance |
| Surface Treatment | Hot-rolled alkaline cleaning surface |
| Electrolytic polish surface | |
| Cold-rolled surface | |
| Machined surface | |
| Technology | extrusion, forging and rolling |
| Test and Quality | dimension inspection |
| appearance quality test | |
| process performance test | |
| mechanical properities test | |
| The specification would be changed by the customers’ requirements. | |
Specification
| Width, mm | Thickness, mm | Thickness deviation, min, mm | Flatness, % | |||
| <300mm | >0.13mm | ±0.025mm | 4% | |||
| ≥300mm | >0.25mm | ±0.06mm | 5%-8% | |||
| Purity(%) | Ag | Ni | P | Cu | Pb | N |
| <0.0001 | <0.0005 | <0.001 | <0.0001 | <0.0001 | <0.002 | |
| Si | Mg | Ca | Sn | Ba | Cd | |
| <0.001 | <0.0001 | <0.001 | <0.0001 | <0.0003 | <0.001 | |
| Na | C | Fe | O | H | Mo | |
| <0.0024 | <0.0033 | <0.0016 | <0.0062 | <0.0006 | >99.97 | |
Specification
| Specifications for molybdenum wire: | ||
| Molybdenum Wire Types | Diameter (inch) | Tolerance (%) |
| Molybdenum Wire for EDM | 0.0024″ ~ 0.01″ | ±3% wt |
| Molybdenum Spray Wire | 1/16″ ~ 1/8″ | ±1% to 3% wt |
| Molybdenum Wire | 0.002″ ~ 0.08″ | ±3% wt |
| Molybdenum Wire(clean) | 0.006″ ~ 0.04″ | ±3% wt |
Specificantions Range
1) Thickness: Hot-rolled plate:1.5~40mm; Cold-rolled plate/sheet:0.05~3.0mm
2) Width: Hot-rolled plate:≤750mm; Cold-rolled plate/sheet: ≤1050mm;
3) Length: Hot-rolled plate:≤3500mm; Cold-rolled plate/sheet: ≤2500mm
Application
| Classification | Feature | Application field |
| Pure Mo plate | High melting point, high purity, low thermal expansivity, excellent thermal conductivity, welding performance and processability | Widely used for manufacturing electron (ion) beam sputtering target, spare parts for ion implantation machine, heat sink of semiconductor, parts of electron tube, MOCVD equipment, and medical device, hot zone, crucible and supporting elements for sapphire crystal furnace, heater, heat shield, supporting element, and boat for vacuum and hydrogen shielded heating furnace |
| Pure Mo plate treated in high temperature | High-purity, consistent in physical and chemical property, and excellent high temperature anti-deforming capability | Suitable for manufacturing base plate for precision electronic ceramics and rear-earth material |
| Lanthanum-doped Mo plate | By using oxide dispersion strengthening mechanism, certain plastic deformation could be performed under room temperature after being treated in high temperature because of its high strength, high recrystallization temperature and excellent high-temperature strength and improved recrystallization brittleness and high temperature anti-deforming capability | particularly suitable for fabricating components used in more than 1500℃ work environment, such as heater, heat shield, base plate and boat for high temperature furnace |
| Lanthanum-doped Mo plate treated in high temperature | Excellent high-temperature strength, and low high temperature deformation due to its oxide dispersion strengthening effect and specific structure | suitable for making base plate for sintering fine ceramics and rear-earth ceramic, bearing rack, base plate and coat for high temperature heating furnace |
| Doped Mo plate | High temperature strength, low recrystallization temperature, and excellent high-temperature creep resistant performance because of its potassium bubble strengthening mechanism | particularly suitable for fabricating products with low high-temperature creep, such as components for electron tube, heater, heat shield, and so on for high temperature furnace |
| Doped Mo plate treated in high temperature | Low high-temperature creep due to its long grain staggered structure and high purity | suitable for making products with high requirement to purity and high-temperature creep, such as base plate for electronic ceramics sintering or heat-treating, supporting elements in electron tube, and so on |
| Cross-rolled pure Mo plate | Low anisotropy and good bending performance | particularly suitable for elongating, spinning, reinforcing and bending, and making elongating or spinning Mo crucible, Mo parts need to reinforce or bend, such as corrugated sheet, bending piece, Mo boat, and so on |
| Cross-rolled pure Mo plate treated in high temperature | Low anisotropy and good bending performance besides same performance of Lanthanum-doped Mo plate | particularly suitable for reinforcing and bending, and making reinforced or bended Mo parts with high temperature requirement, such as heating zone, bended fabricated parts, high-temperature Mo boat, and so on |
Product detail pictures:
Related Product Guide:
Being supported by an state-of-the-art and skilled IT team, we could supply technical support on pre-sales & after-sales service for Hot-selling Sintering Molybdenum Bar - 99.95 Molybdenum Pure Molybdenum Product Moly Sheet Moly Plate Moly Foil In High Temperature Furnaces And Associated Equipment – HSG Metal , The product will supply to all over the world, such as: Kenya, Jakarta, Bangkok, Most problems between suppliers and clients are due to poor communication. Culturally, suppliers can be reluctant to question items they do not understand. We break down people barriers to ensure you get what you want to the level you expect, when you want it. Faster delivery time and the product you want is our Criterion .
By Anna from Greece - 2017.07.28 15:46
This manufacturer can keep improving and perfecting products and service, it is in line with the rules of market competition, a competitive company.
By Dominic from Munich - 2018.02.08 16:45
Related products
-
Good quality Tungsten Scrap Price Per Pound - ...
Product Parameters Brand HSG Standard ASTMB760-07;GB/T3875-83 Grade W1,W2,WAL1,WAL2 Density 19.2g/cc Purity ≥99.95% Size Thick0.05mm min*Width300mm max*L1000mm max Surface Black/Alkali cleaning/ polished Melting point 3260C Process hot rolling chemical composition Chemical composition Impurity content ( % ), ≤ Al Ca Fe Mg Mo Ni Si C N O Balance 0.002 0.005 0.005 0.003 0.01 0.003 0.005 0.008 0.003 0.005 Dimension and permissible variations ...
-
Ferro-Molybdenum - Hot Selling Best Price 99.9...
Product Parameters Item name Hot Selling Best Price 99.95%min. Purity Molybdenum Crucible /Pot for Melting Purity 99.97% Mo Working temperature 1300-1400Centigrade:Mo1 2000 Centigrade:TZM 1700-1900Centigrade: MLa Delivery time 10-15 days Other Material TZM, MHC, MO-W, MO-RE, MO-LA，Mo1 Dimension & Cubage According to your needs or drawings Surface Finish turning, Grinding Density 1.Sintering molybdenum crucible Density: >9.8g/cm3; 2.Forging molybdenum crucible D...
-
Metallic Cobalt - High Pure 99.8% titanium gra...
Product parameters Product name Titanium target for pvd coating machine Grade Titanium (Gr1, Gr2, Gr5, Gr7,GR12) Alloy target: Ti-Al, Ti-Cr, Ti-Zr etc Origin Baoji city Shaanxi Province china Titanium content ≥99.5 (%) Impurity content <0.02 (%) Density 4.51 or 4.50 g/cm3 Standard ASTM B381; ASTM F67, ASTM F136 Size 1. Round target: Ø30–2000mm, thickness 3.0mm–300mm; 2. Plate Targe: Length: 200-500mm Width:100-230mm Thickness:3–40mm; 3. Tube target: Dia...
-
Wolfram Scrap - Tantalum Target – HSG Metal
Product parameters Product Name：high purity tantalum target pure tantalum target Material Tantalum Purity 99.95%min or 99.99%min Color A shiny, silvery metal that is very resistant to corrosion. Other name Ta target Standard ASTM B 708 Size Dia >10mm * thick >0.1mm Shape Planar MOQ 5pcs Delivery time 7days Used Sputtering Coating Machines Table 1: Chemical composition Chemistry (%) Designation Chief component Impurities maxmium Ta Nb Fe...
-
Ferro Moly - China Ferro Molybdenum Factory Su...
Chemical Composition FeMo composition (%) Grade Mo Si S P C Cu FeMo70 65-75 2 0.08 0.05 0.1 0.5 FeMo60-A 60-65 1 0.08 0.04 0.1 0.5 FeMo60-B 60-65 1.5 0.1 0.05 0.1 0.5 FeMo60-C 60-65 2 0.15 0.05 0.15 1 FeMo55-A 55-60 1 0.1 0.08 0.15 0.5 FeMo55-B 55-60 1.5 0.15 0.1 0.2 0.5 Products Description Ferro Molybdenum70 is mainly used to add molybdenum to steel in steel making. Molybde...
-
Ferrovanadium - HSG Ferro Tungsten price for s...
We supply Ferro Tungsten of all grades as follows Grade FeW 8OW-A FeW80-B FEW 80-C W 75%-80% 75%-80% 75%-80% C 0.1% max 0.3% max 0.6% max P 0.03% max 0.04% max 0.05% max S 0.06% max 0.07% max 0.08% max Si 0.5% max 0.7% max 0.7% max Mn 0.25% max 0.35% max 0.5% max Sn 0.06% max 0.08% max 0.1% max Cu 0.1% max 0.12% max 0.15% max As 0.06% max 0.08% max 0.10% max Bi 0.05% max 0.05% max 0.0...