High definition Moly Scrap - Niobium Target – HSG Metal
High definition Moly Scrap - Niobium Target – HSG Metal Detail:
Product parameters
| Specification | |
| Item | ASTM B393 9995 pure polished niobium target for industry |
| Standard | ASTM B393 |
| Density | 8.57g/cm3 |
| Purity | ≥99.95% |
| Size | according to customer’s drawings |
| Inspection | Chemical composition testing, Mechanical testing, Ultrasonic inspection, Appearance size detection |
| Grade | R04200, R04210, R04251, R04261 |
| Surface | polishing, grinding |
| Technique | sintered, rolled, forged |
| Feature | High temperature resistance, corrosion resistance |
| Application | Superconducting industry, Aerospace aviation, Chmeical Industry, Mechanical |
|
Chemical Composition |
|||
| Grade |
R04200 |
R04210 |
|
| Main element |
Nb |
Bal |
Bal |
| Impurity elements |
Fe |
0.004 |
0.01 |
|
Si |
0.004 |
0.01 |
|
|
Ni |
0.002 |
0.005 |
|
|
W |
0.005 |
0.02 |
|
|
Mo |
0.005 |
0.01 |
|
|
Ti |
0.002 |
0.004 |
|
|
Ta |
0.005 |
0.07 |
|
|
O |
0.012 |
0.015 |
|
|
C |
0.035 |
0.005 |
|
|
H |
0.012 |
0.0015 |
|
|
N |
0.003 |
0.008 |
|
|
Mechanical Property |
|||
|
Grade |
Tensile Strength ≥ Mpa |
Yield Strength ≥ Mpa(0.2% residual deformation) |
Extend Rate % (25.4mm measurement) |
|
R04200 R04210 |
125 |
85 |
25 |
|
Content, Max, Weight % |
||||
|
Element |
Grand: R04200 |
Grand:R04210 |
Grand:R04251 |
Grand:R04261 |
|
Unalloyed Niobium |
Unalloyed Niobium |
(Reactor grade niobium-1% Zirconium) |
(Commercial grade niobium-1% Zirconium) |
|
|
C |
0.01 |
0.01 |
0.01 |
0.01 |
|
O |
0.015 |
0.025 |
0.015 |
0.025 |
|
N |
0.01 |
0.01 |
0.01 |
0.01 |
|
H |
0.0015 |
0.0015 |
0.0015 |
0.0015 |
|
Fe |
0.005 |
0.01 |
0.005 |
0.01 |
|
Mo |
0.01 |
0.02 |
0.01 |
0.05 |
|
Ta |
0.1 |
0.3 |
0.1 |
0.5 |
|
Ni |
0.005 |
0.005 |
0.005 |
0.005 |
|
Si |
0.005 |
0.005 |
0.005 |
0.005 |
|
Ti |
0.02 |
0.03 |
0.02 |
0.03 |
|
W |
0.03 |
0.05 |
0.03 |
0.05 |
|
Zr |
0.02 |
0.02 |
0.8~1.2 |
0.8~1.2 |
|
Nb |
Remainder |
Remainder |
Remainder |
Remainder |
Product technology
The vacuum electron beam melting process produces niobium plates. The unforged niobium bar is first smelted into a niobium ingot through a vacuum electron beam melting furnace. It is usually divided into single smelting and multiple smelting. We usually use twice smelted niobium ingots. Depending on the product requirements, we can perform more than two smelting.
Application
Superconducting industry
Used to produce niobium foil
Heat shield in high temperature furnace
Used to produce niobium welded pipe
Used in the production of human implants.
Product detail pictures:
Related Product Guide:
Together with the "Client-Oriented" enterprise philosophy, a arduous good quality control technique, sophisticated producing equipment and a sturdy R&D staff, we generally offer superior quality merchandise, superb solutions and aggressive rates for High definition Moly Scrap - Niobium Target – HSG Metal , The product will supply to all over the world, such as: Kuwait, Berlin, Israel, If you need to have any of our merchandise, or have other items to be produced, make sure you send us your inquiries, samples or in depth drawings. Meanwhile, aiming to develop into an international enterprise group, we look forward to receiving offers for joint ventures and other cooperative projects.
By Muriel from Namibia - 2018.12.05 13:53
The goods are very perfect and the company sales manager is warmful, we will come to this company to purchase next time.
By Phoebe from Philadelphia - 2018.12.30 10:21
Related products
-
Ferro Molybdenum Welding Materials - 99.95 Mol...
Product Parameters Item molybdenum sheet/plate Grade Mo1, Mo2 Stock size 0.2mm, 0.5mm, 1mm, 2mm MOQ hot rolling, cleaning, polished Stock 1 kilograms Property anti-corrosion, high temperature resistance Surface Treatment Hot-rolled alkaline cleaning surface Electrolytic polish surface Cold-rolled surface Machined surface Technology extrusion, forging and rolling Test and Quality dimension inspection appearance quality test process performance test mechanical pro...
-
Metal Chrome - GOOD QUALITY PURE CHROMIUM CHRO...
Metal Chromium Lump / Cr Lmup Grade Chemical Composition % Cr Fe Si Al Cu C S P ≧ ≦ HRCR99-A 99 0.30 0.25 0.30 0.01 0.01 0.01 0.01 HRCR99-B 99 0.40 0.30 0.30 0.00 0.02 0.02 0.01 HRCR98.5-A 98.5 0.45 0.35 0.50 0.04 0.03 0.02 0.01 HRCR98.5-B 98.5 0.50 0.40 0.50 0.06 0.03 0.02 0.01 HRCR98 98 0.80 0.40 0.80 0.02 0.05 0.03 0.01 Description Metal chromi...
-
100% Original Unwrought Tungsten Bar - Manufac...
Product Parameters Product Name tungsten rectangular bar Material tungsten Surface Polished,swaged,ground Density 19.3g/cm3 Feature High density, Good machinability, Good mechanical properties, High absorption capacity against X rays and gamma rays Purity W≥99.95% Size As per your request Products Description Manufacturer supply High quality 99.95% Tungsten rectangular bar can be manufactured in random length pieces or cut to meet customers’ desired lengths. There are ...
-
Excellent quality Tungsten Carbide Scrap Value ...
Product Parameters Tungsten Block Polished 1kg Tungsten Cube 38.1mm Purity W≥99.95% Standard ASTM B760, GB-T 3875, ASTM B777 Surface Ground Surface, Machined surface Density 18.5 g/cm3 –19.2 g/cm3 Dimensions Common sizes：12.7*12.7*12.7mm20*20*20mm 25.4*25.4*25.4mm 38.1*38.1*38.1mm Application Ornament, decoration, Balance weight, desktop, gift, target, Military industry, and so on The characteristics 1. Laser engraving tungsten cube for 1kg 2. Melting point ...
-
Indium Ingot - Tantalum Target – HSG Metal
Product parameters Product Name：high purity tantalum target pure tantalum target Material Tantalum Purity 99.95%min or 99.99%min Color A shiny, silvery metal that is very resistant to corrosion. Other name Ta target Standard ASTM B 708 Size Dia >10mm * thick >0.1mm Shape Planar MOQ 5pcs Delivery time 7days Used Sputtering Coating Machines Table 1: Chemical composition Chemistry (%) Designation Chief component Impurities maxmium Ta Nb Fe...
-
Hot New Products Ferro Moly Prijs - Ferro Vana...
Specification of Ferrovanadium Brand Chemical Compositions (%) V C Si P S Al Mn ≤ FeV40-A 38.0~45.0 0.60 2.0 0.08 0.06 1.5 — FeV40-B 38.0~45.0 0.80 3.0 0.15 0.10 2.0 — FeV50-A 48.0~55.0 0.40 2.0 0.06 0.04 1.5 — FeV50-B 48.0~55.0 0.60 2.5 0.10 0.05 2.0 — FeV60-A 58.0~65.0 0.40 2.0 0.06 0.04 1.5 — FeV60-B 58.0~65.0 0.60 2.5 0.10 0.05 2...