Good Quality Cobalt Metal - Niobium Target – HSG Metal
Good Quality Cobalt Metal - Niobium Target – HSG Metal Detail:
Product parameters
| Specification | |
| Item | ASTM B393 9995 pure polished niobium target for industry |
| Standard | ASTM B393 |
| Density | 8.57g/cm3 |
| Purity | ≥99.95% |
| Size | according to customer’s drawings |
| Inspection | Chemical composition testing, Mechanical testing, Ultrasonic inspection, Appearance size detection |
| Grade | R04200, R04210, R04251, R04261 |
| Surface | polishing, grinding |
| Technique | sintered, rolled, forged |
| Feature | High temperature resistance, corrosion resistance |
| Application | Superconducting industry, Aerospace aviation, Chmeical Industry, Mechanical |
|
Chemical Composition |
|||
| Grade |
R04200 |
R04210 |
|
| Main element |
Nb |
Bal |
Bal |
| Impurity elements |
Fe |
0.004 |
0.01 |
|
Si |
0.004 |
0.01 |
|
|
Ni |
0.002 |
0.005 |
|
|
W |
0.005 |
0.02 |
|
|
Mo |
0.005 |
0.01 |
|
|
Ti |
0.002 |
0.004 |
|
|
Ta |
0.005 |
0.07 |
|
|
O |
0.012 |
0.015 |
|
|
C |
0.035 |
0.005 |
|
|
H |
0.012 |
0.0015 |
|
|
N |
0.003 |
0.008 |
|
|
Mechanical Property |
|||
|
Grade |
Tensile Strength ≥ Mpa |
Yield Strength ≥ Mpa(0.2% residual deformation) |
Extend Rate % (25.4mm measurement) |
|
R04200 R04210 |
125 |
85 |
25 |
|
Content, Max, Weight % |
||||
|
Element |
Grand: R04200 |
Grand:R04210 |
Grand:R04251 |
Grand:R04261 |
|
Unalloyed Niobium |
Unalloyed Niobium |
(Reactor grade niobium-1% Zirconium) |
(Commercial grade niobium-1% Zirconium) |
|
|
C |
0.01 |
0.01 |
0.01 |
0.01 |
|
O |
0.015 |
0.025 |
0.015 |
0.025 |
|
N |
0.01 |
0.01 |
0.01 |
0.01 |
|
H |
0.0015 |
0.0015 |
0.0015 |
0.0015 |
|
Fe |
0.005 |
0.01 |
0.005 |
0.01 |
|
Mo |
0.01 |
0.02 |
0.01 |
0.05 |
|
Ta |
0.1 |
0.3 |
0.1 |
0.5 |
|
Ni |
0.005 |
0.005 |
0.005 |
0.005 |
|
Si |
0.005 |
0.005 |
0.005 |
0.005 |
|
Ti |
0.02 |
0.03 |
0.02 |
0.03 |
|
W |
0.03 |
0.05 |
0.03 |
0.05 |
|
Zr |
0.02 |
0.02 |
0.8~1.2 |
0.8~1.2 |
|
Nb |
Remainder |
Remainder |
Remainder |
Remainder |
Product technology
The vacuum electron beam melting process produces niobium plates. The unforged niobium bar is first smelted into a niobium ingot through a vacuum electron beam melting furnace. It is usually divided into single smelting and multiple smelting. We usually use twice smelted niobium ingots. Depending on the product requirements, we can perform more than two smelting.
Application
Superconducting industry
Used to produce niobium foil
Heat shield in high temperature furnace
Used to produce niobium welded pipe
Used in the production of human implants.
Product detail pictures:
Related Product Guide:
That has a positive and progressive attitude to customer's interest, our organization consistently improves our products quality to satisfy the demands of shoppers and further focuses on safety, reliability, environmental specifications, and innovation of Good Quality Cobalt Metal - Niobium Target – HSG Metal , The product will supply to all over the world, such as: United States, Eindhoven, belarus, We will continue to devote ourselves to market & product development and build a well-knit service to our customer to create a more prosperous future. Please contact us today to find out how we can work together.
By Lisa from Ukraine - 2017.08.16 13:39
The company has rich resources, advanced machinery, experienced workers and excellent services, hope you keep improving and perfecting your products and service, wish you better!
By Kevin Ellyson from Bulgaria - 2018.12.11 11:26
Related products
-
Tungsten Scrap For Sale - Factory 0.05mm~2.00m...
Specification Rand WAL1,WAL2 W1,W2 Black wire White wire Min Diameter(mm) 0.02 0.005 0.4 Max Diameter(mm) 1.8 0.35 0.8 Products Description 1. Purity:99.95% W1 2. Density: 19.3g/cm3 3. Grade:W1,W2,WAL1,WAL2 4. Shape:as your drawing. 5. Feature:High melting point, high temperature oxidation resistance, long service life, resistance to corrosion The chemical composition of tungsten wire Brand Tungsten Content /%≥ The sum of impurity elements /%≤ The content of ...
-
Hot-selling Ferro Vanadium Prijs - China Ferro...
Chemical Composition FeMo composition (%) Grade Mo Si S P C Cu FeMo70 65-75 2 0.08 0.05 0.1 0.5 FeMo60-A 60-65 1 0.08 0.04 0.1 0.5 FeMo60-B 60-65 1.5 0.1 0.05 0.1 0.5 FeMo60-C 60-65 2 0.15 0.05 0.15 1 FeMo55-A 55-60 1 0.1 0.08 0.15 0.5 FeMo55-B 55-60 1.5 0.15 0.1 0.2 0.5 Products Description Ferro Molybdenum70 is mainly used to add molybdenum to steel in steel making. Molybde...
-
99.995 Indium Ingot - High Pure 99.8% titanium...
Product parameters Product name Titanium target for pvd coating machine Grade Titanium (Gr1, Gr2, Gr5, Gr7,GR12) Alloy target: Ti-Al, Ti-Cr, Ti-Zr etc Origin Baoji city Shaanxi Province china Titanium content ≥99.5 (%) Impurity content <0.02 (%) Density 4.51 or 4.50 g/cm3 Standard ASTM B381; ASTM F67, ASTM F136 Size 1. Round target: Ø30–2000mm, thickness 3.0mm–300mm; 2. Plate Targe: Length: 200-500mm Width:100-230mm Thickness:3–40mm; 3. Tube target: Dia...
-
Ingot Indium - Niobium Target – HSG Metal
Product parameters Specification Item ASTM B393 9995 pure polished niobium target for industry Standard ASTM B393 Density 8.57g/cm3 Purity ≥99.95% Size according to customer’s drawings Inspection Chemical composition testing, Mechanical testing, Ultrasonic inspection, Appearance size detection Grade R04200, R04210, R04251, R04261 Surface polishing, grinding Technique sintered, rolled, forged Feature High temperature resistance, corrosion resistance Application S...
-
Femo 60 Ferromolybdenum - Hot Selling Best Pri...
Product Parameters Item name Hot Selling Best Price 99.95%min. Purity Molybdenum Crucible /Pot for Melting Purity 99.97% Mo Working temperature 1300-1400Centigrade:Mo1 2000 Centigrade:TZM 1700-1900Centigrade: MLa Delivery time 10-15 days Other Material TZM, MHC, MO-W, MO-RE, MO-LA，Mo1 Dimension & Cubage According to your needs or drawings Surface Finish turning, Grinding Density 1.Sintering molybdenum crucible Density: >9.8g/cm3; 2.Forging molybdenum crucible D...
-
Ferro Molybdenum Welding Materials - High Qual...
Product Parameters Product name Pure molybdenum cube / molybdenum block for industry Grade Mo1 Mo2 TZM Type cube, block, ignot,lump Surface Polish/grinding/chemical wash Density 10.2g/cc Processing Rolling, Forging, Sintering Standard ASTM B 386-2003, GB 3876-2007, GB 3877-2006 Size Thickness: min0.01mmWidth: max 650mm Popular size 10*10*10mm / 20*20*20mm / 46*46*46 mm / 58*58*58mm Chemical requirements Element Ni Mg Fe Pb Al Bi Si Cd Ca P Concentration(%) 0.003 0.0...