Ferro Molybdenum Rod - 99.95 Molybdenum Pure Molybdenum Product Moly Sheet Moly Plate Moly Foil In High Temperature Furnaces And Associated Equipment – HSG Metal
Ferro Molybdenum Rod - 99.95 Molybdenum Pure Molybdenum Product Moly Sheet Moly Plate Moly Foil In High Temperature Furnaces And Associated Equipment – HSG Metal Detail:
Product Parameters
| Item | molybdenum sheet/plate |
| Grade | Mo1, Mo2 |
| Stock size | 0.2mm, 0.5mm, 1mm, 2mm |
| MOQ | hot rolling, cleaning, polished |
| Stock | 1 kilograms |
| Property | anti-corrosion, high temperature resistance |
| Surface Treatment | Hot-rolled alkaline cleaning surface |
| Electrolytic polish surface | |
| Cold-rolled surface | |
| Machined surface | |
| Technology | extrusion, forging and rolling |
| Test and Quality | dimension inspection |
| appearance quality test | |
| process performance test | |
| mechanical properities test | |
| The specification would be changed by the customers’ requirements. | |
Specification
| Width, mm | Thickness, mm | Thickness deviation, min, mm | Flatness, % | |||
| <300mm | >0.13mm | ±0.025mm | 4% | |||
| ≥300mm | >0.25mm | ±0.06mm | 5%-8% | |||
| Purity(%) | Ag | Ni | P | Cu | Pb | N |
| <0.0001 | <0.0005 | <0.001 | <0.0001 | <0.0001 | <0.002 | |
| Si | Mg | Ca | Sn | Ba | Cd | |
| <0.001 | <0.0001 | <0.001 | <0.0001 | <0.0003 | <0.001 | |
| Na | C | Fe | O | H | Mo | |
| <0.0024 | <0.0033 | <0.0016 | <0.0062 | <0.0006 | >99.97 | |
Specification
| Specifications for molybdenum wire: | ||
| Molybdenum Wire Types | Diameter (inch) | Tolerance (%) |
| Molybdenum Wire for EDM | 0.0024″ ~ 0.01″ | ±3% wt |
| Molybdenum Spray Wire | 1/16″ ~ 1/8″ | ±1% to 3% wt |
| Molybdenum Wire | 0.002″ ~ 0.08″ | ±3% wt |
| Molybdenum Wire(clean) | 0.006″ ~ 0.04″ | ±3% wt |
Specificantions Range
1) Thickness: Hot-rolled plate:1.5~40mm; Cold-rolled plate/sheet:0.05~3.0mm
2) Width: Hot-rolled plate:≤750mm; Cold-rolled plate/sheet: ≤1050mm;
3) Length: Hot-rolled plate:≤3500mm; Cold-rolled plate/sheet: ≤2500mm
Application
| Classification | Feature | Application field |
| Pure Mo plate | High melting point, high purity, low thermal expansivity, excellent thermal conductivity, welding performance and processability | Widely used for manufacturing electron (ion) beam sputtering target, spare parts for ion implantation machine, heat sink of semiconductor, parts of electron tube, MOCVD equipment, and medical device, hot zone, crucible and supporting elements for sapphire crystal furnace, heater, heat shield, supporting element, and boat for vacuum and hydrogen shielded heating furnace |
| Pure Mo plate treated in high temperature | High-purity, consistent in physical and chemical property, and excellent high temperature anti-deforming capability | Suitable for manufacturing base plate for precision electronic ceramics and rear-earth material |
| Lanthanum-doped Mo plate | By using oxide dispersion strengthening mechanism, certain plastic deformation could be performed under room temperature after being treated in high temperature because of its high strength, high recrystallization temperature and excellent high-temperature strength and improved recrystallization brittleness and high temperature anti-deforming capability | particularly suitable for fabricating components used in more than 1500℃ work environment, such as heater, heat shield, base plate and boat for high temperature furnace |
| Lanthanum-doped Mo plate treated in high temperature | Excellent high-temperature strength, and low high temperature deformation due to its oxide dispersion strengthening effect and specific structure | suitable for making base plate for sintering fine ceramics and rear-earth ceramic, bearing rack, base plate and coat for high temperature heating furnace |
| Doped Mo plate | High temperature strength, low recrystallization temperature, and excellent high-temperature creep resistant performance because of its potassium bubble strengthening mechanism | particularly suitable for fabricating products with low high-temperature creep, such as components for electron tube, heater, heat shield, and so on for high temperature furnace |
| Doped Mo plate treated in high temperature | Low high-temperature creep due to its long grain staggered structure and high purity | suitable for making products with high requirement to purity and high-temperature creep, such as base plate for electronic ceramics sintering or heat-treating, supporting elements in electron tube, and so on |
| Cross-rolled pure Mo plate | Low anisotropy and good bending performance | particularly suitable for elongating, spinning, reinforcing and bending, and making elongating or spinning Mo crucible, Mo parts need to reinforce or bend, such as corrugated sheet, bending piece, Mo boat, and so on |
| Cross-rolled pure Mo plate treated in high temperature | Low anisotropy and good bending performance besides same performance of Lanthanum-doped Mo plate | particularly suitable for reinforcing and bending, and making reinforced or bended Mo parts with high temperature requirement, such as heating zone, bended fabricated parts, high-temperature Mo boat, and so on |
Product detail pictures:
Related Product Guide:
Our purpose would be to offer good quality products at competitive price ranges, and top-notch support to clients around the whole world. We're ISO9001, CE, and GS certified and strictly adhere to their good quality specifications for Ferro Molybdenum Rod - 99.95 Molybdenum Pure Molybdenum Product Moly Sheet Moly Plate Moly Foil In High Temperature Furnaces And Associated Equipment – HSG Metal , The product will supply to all over the world, such as: San Francisco, Japan, belarus, Our company mission is that providing high quality and beautiful products with reasonable price and strive to gain 100% good reputation from our clients. We believe Profession achieves excellence! We welcome you to cooperate with us and grow up together.
By Bruno Cabrera from USA - 2017.04.08 14:55
The sales person is professional and responsible, warm and polite, we had a pleasant conversation and no language barriers on communication.
By Hulda from Belarus - 2017.08.18 11:04
Related products
-
Ferro Moly - China Ferro Molybdenum Factory Su...
Chemical Composition FeMo composition (%) Grade Mo Si S P C Cu FeMo70 65-75 2 0.08 0.05 0.1 0.5 FeMo60-A 60-65 1 0.08 0.04 0.1 0.5 FeMo60-B 60-65 1.5 0.1 0.05 0.1 0.5 FeMo60-C 60-65 2 0.15 0.05 0.15 1 FeMo55-A 55-60 1 0.1 0.08 0.15 0.5 FeMo55-B 55-60 1.5 0.15 0.1 0.2 0.5 Products Description Ferro Molybdenum70 is mainly used to add molybdenum to steel in steel making. Molybde...
-
Tungsten Scrap Price Per Pound - Customized Hi...
Product Parameters Material tungsten Color sintered, sandblasting or polishing Purity 99.95% Tungsten Grade W1,W2,WAL,WLa,WNiFe Product Feature High melting point, High- density, high temperature oxidation resistance, long service life, resistance to corrosion. Property high hardness and strength, excellent corrosion resistance Desity 19.3/cm3 Dimension Customized Standard ASTM B760 Melting point 3410℃ Design&Size OEM or ODM acceptable Chemical Compositio...
-
Metal Chrome - GOOD QUALITY PURE CHROMIUM CHRO...
Metal Chromium Lump / Cr Lmup Grade Chemical Composition % Cr Fe Si Al Cu C S P ≧ ≦ HRCR99-A 99 0.30 0.25 0.30 0.01 0.01 0.01 0.01 HRCR99-B 99 0.40 0.30 0.30 0.00 0.02 0.02 0.01 HRCR98.5-A 98.5 0.45 0.35 0.50 0.04 0.03 0.02 0.01 HRCR98.5-B 98.5 0.50 0.40 0.50 0.06 0.03 0.02 0.01 HRCR98 98 0.80 0.40 0.80 0.02 0.05 0.03 0.01 Description Metal chromi...
-
Few Ferro Tungsten - Oem&Odm High Hardness...
Product Parameters Product Name Tungsten cube/cylinder Material Pure tungsten and tungsten heavy alloy Application Ornament, decoration, Balance weight, target, Military industry, and so on Shape cube,cylinder,block,granule etc. Standard ASTM B760, GB-T 3875, ASTM B777 Processing Rolling, Forging, Sintering Surface Polish, alkali cleaning Density 18.0 g/cm3 –19.3 g/cm3 pure tungsten and W-Ni-Fe tungsten alloy cube/block: 6*6*6mm 12.7*12.7*12.7mm 20*20*20mm 38.1*38...
-
Tungsten Scrap Price Per Pound - High Density ...
Product Parameters Tungsten Block Polished 1kg Tungsten Cube 38.1mm Purity W≥99.95% Standard ASTM B760, GB-T 3875, ASTM B777 Surface Ground Surface, Machined surface Density 18.5 g/cm3 –19.2 g/cm3 Dimensions Common sizes：12.7*12.7*12.7mm20*20*20mm 25.4*25.4*25.4mm 38.1*38.1*38.1mm Application Ornament, decoration, Balance weight, desktop, gift, target, Military industry, and so on The characteristics 1. Laser engraving tungsten cube for 1kg 2. Melting point ...
-
Wholesale Price China Ferromolybdenum Fe-Mo - ...
Product Parameters Term Molybdenum bar Grade Mo1,Mo2,TZM,Mla,etc Size as request Surface condition hot rolling, cleaning, polishedc MOQ 1 kilograms Test and Quality dimension inspection appearance quality test process performance test mechanical properities test Load port shanghai shenzhen qingdao Packing standard wooden case, carton or as request Payment L/C, D/A, D/P, T/T, Western union, MoneyGram, Paypal, Wire-transfer Delivery time 10-15 working days ...