Cobalt Metal Plate - Niobium Target – HSG Metal
Cobalt Metal Plate - Niobium Target – HSG Metal Detail:
Product parameters
| Specification | |
| Item | ASTM B393 9995 pure polished niobium target for industry |
| Standard | ASTM B393 |
| Density | 8.57g/cm3 |
| Purity | ≥99.95% |
| Size | according to customer’s drawings |
| Inspection | Chemical composition testing, Mechanical testing, Ultrasonic inspection, Appearance size detection |
| Grade | R04200, R04210, R04251, R04261 |
| Surface | polishing, grinding |
| Technique | sintered, rolled, forged |
| Feature | High temperature resistance, corrosion resistance |
| Application | Superconducting industry, Aerospace aviation, Chmeical Industry, Mechanical |
|
Chemical Composition |
|||
| Grade |
R04200 |
R04210 |
|
| Main element |
Nb |
Bal |
Bal |
| Impurity elements |
Fe |
0.004 |
0.01 |
|
Si |
0.004 |
0.01 |
|
|
Ni |
0.002 |
0.005 |
|
|
W |
0.005 |
0.02 |
|
|
Mo |
0.005 |
0.01 |
|
|
Ti |
0.002 |
0.004 |
|
|
Ta |
0.005 |
0.07 |
|
|
O |
0.012 |
0.015 |
|
|
C |
0.035 |
0.005 |
|
|
H |
0.012 |
0.0015 |
|
|
N |
0.003 |
0.008 |
|
|
Mechanical Property |
|||
|
Grade |
Tensile Strength ≥ Mpa |
Yield Strength ≥ Mpa(0.2% residual deformation) |
Extend Rate % (25.4mm measurement) |
|
R04200 R04210 |
125 |
85 |
25 |
|
Content, Max, Weight % |
||||
|
Element |
Grand: R04200 |
Grand:R04210 |
Grand:R04251 |
Grand:R04261 |
|
Unalloyed Niobium |
Unalloyed Niobium |
(Reactor grade niobium-1% Zirconium) |
(Commercial grade niobium-1% Zirconium) |
|
|
C |
0.01 |
0.01 |
0.01 |
0.01 |
|
O |
0.015 |
0.025 |
0.015 |
0.025 |
|
N |
0.01 |
0.01 |
0.01 |
0.01 |
|
H |
0.0015 |
0.0015 |
0.0015 |
0.0015 |
|
Fe |
0.005 |
0.01 |
0.005 |
0.01 |
|
Mo |
0.01 |
0.02 |
0.01 |
0.05 |
|
Ta |
0.1 |
0.3 |
0.1 |
0.5 |
|
Ni |
0.005 |
0.005 |
0.005 |
0.005 |
|
Si |
0.005 |
0.005 |
0.005 |
0.005 |
|
Ti |
0.02 |
0.03 |
0.02 |
0.03 |
|
W |
0.03 |
0.05 |
0.03 |
0.05 |
|
Zr |
0.02 |
0.02 |
0.8~1.2 |
0.8~1.2 |
|
Nb |
Remainder |
Remainder |
Remainder |
Remainder |
Product technology
The vacuum electron beam melting process produces niobium plates. The unforged niobium bar is first smelted into a niobium ingot through a vacuum electron beam melting furnace. It is usually divided into single smelting and multiple smelting. We usually use twice smelted niobium ingots. Depending on the product requirements, we can perform more than two smelting.
Application
Superconducting industry
Used to produce niobium foil
Heat shield in high temperature furnace
Used to produce niobium welded pipe
Used in the production of human implants.
Product detail pictures:
Related Product Guide:
The key to our success is "Good Product or service High quality, Reasonable Rate and Efficient Service" for Cobalt Metal Plate - Niobium Target – HSG Metal , The product will supply to all over the world, such as: Cyprus, Morocco, Brazil, We also have the strong ability of integration to supply our best service, and plan to build the warehouse in the different countries around the world, that will be more conveniently to service our customers.
By Hulda from Argentina - 2017.10.13 10:47
The after-sale warranty service is timely and thoughtful, encounter problems can be resolved very quickly, we feel reliable and secure.
By Margaret from Singapore - 2018.02.21 12:14
Related products
-
Good Quality Metal Chrome - GOOD QUALITY PURE ...
Metal Chromium Lump / Cr Lmup Grade Chemical Composition % Cr Fe Si Al Cu C S P ≧ ≦ HRCR99-A 99 0.30 0.25 0.30 0.01 0.01 0.01 0.01 HRCR99-B 99 0.40 0.30 0.30 0.00 0.02 0.02 0.01 HRCR98.5-A 98.5 0.45 0.35 0.50 0.04 0.03 0.02 0.01 HRCR98.5-B 98.5 0.50 0.40 0.50 0.06 0.03 0.02 0.01 HRCR98 98 0.80 0.40 0.80 0.02 0.05 0.03 0.01 Description Metal chromi...
-
Chinese wholesale Femo 60 Ferromolybdeen - Chi...
Chemical Composition FeMo composition (%) Grade Mo Si S P C Cu FeMo70 65-75 2 0.08 0.05 0.1 0.5 FeMo60-A 60-65 1 0.08 0.04 0.1 0.5 FeMo60-B 60-65 1.5 0.1 0.05 0.1 0.5 FeMo60-C 60-65 2 0.15 0.05 0.15 1 FeMo55-A 55-60 1 0.1 0.08 0.15 0.5 FeMo55-B 55-60 1.5 0.15 0.1 0.2 0.5 Products Description Ferro Molybdenum70 is mainly used to add molybdenum to steel in steel making. Molybde...
-
Metal Chrome - GOOD QUALITY PURE CHROMIUM CHRO...
Metal Chromium Lump / Cr Lmup Grade Chemical Composition % Cr Fe Si Al Cu C S P ≧ ≦ HRCR99-A 99 0.30 0.25 0.30 0.01 0.01 0.01 0.01 HRCR99-B 99 0.40 0.30 0.30 0.00 0.02 0.02 0.01 HRCR98.5-A 98.5 0.45 0.35 0.50 0.04 0.03 0.02 0.01 HRCR98.5-B 98.5 0.50 0.40 0.50 0.06 0.03 0.02 0.01 HRCR98 98 0.80 0.40 0.80 0.02 0.05 0.03 0.01 Description Metal chromi...
-
Hot-selling Sintering Molybdenum Bar - Hot Sel...
Product Parameters Item name Hot Selling Best Price 99.95%min. Purity Molybdenum Crucible /Pot for Melting Purity 99.97% Mo Working temperature 1300-1400Centigrade:Mo1 2000 Centigrade:TZM 1700-1900Centigrade: MLa Delivery time 10-15 days Other Material TZM, MHC, MO-W, MO-RE, MO-LA，Mo1 Dimension & Cubage According to your needs or drawings Surface Finish turning, Grinding Density 1.Sintering molybdenum crucible Density: >9.8g/cm3; 2.Forging molybdenum crucible D...
-
Factory Cheap Hot Ferro Molybdenum Price Trade ...
Product Parameters Item molybdenum sheet/plate Grade Mo1, Mo2 Stock size 0.2mm, 0.5mm, 1mm, 2mm MOQ hot rolling, cleaning, polished Stock 1 kilograms Property anti-corrosion, high temperature resistance Surface Treatment Hot-rolled alkaline cleaning surface Electrolytic polish surface Cold-rolled surface Machined surface Technology extrusion, forging and rolling Test and Quality dimension inspection appearance quality test process performance test mechanical pro...
-
Professional China Ferro Tungsten Price - High...
Product Parameters Item name High Temperature Resistance 99.95% Pure tungsten crucible melting pot price pure tungsten W Purity: 99.95% Other Material W1,W2,WAL1,WAL2,W-Ni-Fe, W-Ni-Cu,WMO50,WMO20 Density 1.Sintering tungsten crucible Density:18.0 – 18.5 g/cm3; 2.Forging tungsten crucible Density:18.5 – 19.0 g/cm3 Dimension & Cubage According to your needs or drawings Delivery time 10-15 days Application It is widely used for smelting of rare earth metals, heatin...