Cobalt Metal - Niobium Target – HSG Metal
Cobalt Metal - Niobium Target – HSG Metal Detail:
Product parameters
| Specification | |
| Item | ASTM B393 9995 pure polished niobium target for industry |
| Standard | ASTM B393 |
| Density | 8.57g/cm3 |
| Purity | ≥99.95% |
| Size | according to customer’s drawings |
| Inspection | Chemical composition testing, Mechanical testing, Ultrasonic inspection, Appearance size detection |
| Grade | R04200, R04210, R04251, R04261 |
| Surface | polishing, grinding |
| Technique | sintered, rolled, forged |
| Feature | High temperature resistance, corrosion resistance |
| Application | Superconducting industry, Aerospace aviation, Chmeical Industry, Mechanical |
|
Chemical Composition |
|||
| Grade |
R04200 |
R04210 |
|
| Main element |
Nb |
Bal |
Bal |
| Impurity elements |
Fe |
0.004 |
0.01 |
|
Si |
0.004 |
0.01 |
|
|
Ni |
0.002 |
0.005 |
|
|
W |
0.005 |
0.02 |
|
|
Mo |
0.005 |
0.01 |
|
|
Ti |
0.002 |
0.004 |
|
|
Ta |
0.005 |
0.07 |
|
|
O |
0.012 |
0.015 |
|
|
C |
0.035 |
0.005 |
|
|
H |
0.012 |
0.0015 |
|
|
N |
0.003 |
0.008 |
|
|
Mechanical Property |
|||
|
Grade |
Tensile Strength ≥ Mpa |
Yield Strength ≥ Mpa(0.2% residual deformation) |
Extend Rate % (25.4mm measurement) |
|
R04200 R04210 |
125 |
85 |
25 |
|
Content, Max, Weight % |
||||
|
Element |
Grand: R04200 |
Grand:R04210 |
Grand:R04251 |
Grand:R04261 |
|
Unalloyed Niobium |
Unalloyed Niobium |
(Reactor grade niobium-1% Zirconium) |
(Commercial grade niobium-1% Zirconium) |
|
|
C |
0.01 |
0.01 |
0.01 |
0.01 |
|
O |
0.015 |
0.025 |
0.015 |
0.025 |
|
N |
0.01 |
0.01 |
0.01 |
0.01 |
|
H |
0.0015 |
0.0015 |
0.0015 |
0.0015 |
|
Fe |
0.005 |
0.01 |
0.005 |
0.01 |
|
Mo |
0.01 |
0.02 |
0.01 |
0.05 |
|
Ta |
0.1 |
0.3 |
0.1 |
0.5 |
|
Ni |
0.005 |
0.005 |
0.005 |
0.005 |
|
Si |
0.005 |
0.005 |
0.005 |
0.005 |
|
Ti |
0.02 |
0.03 |
0.02 |
0.03 |
|
W |
0.03 |
0.05 |
0.03 |
0.05 |
|
Zr |
0.02 |
0.02 |
0.8~1.2 |
0.8~1.2 |
|
Nb |
Remainder |
Remainder |
Remainder |
Remainder |
Product technology
The vacuum electron beam melting process produces niobium plates. The unforged niobium bar is first smelted into a niobium ingot through a vacuum electron beam melting furnace. It is usually divided into single smelting and multiple smelting. We usually use twice smelted niobium ingots. Depending on the product requirements, we can perform more than two smelting.
Application
Superconducting industry
Used to produce niobium foil
Heat shield in high temperature furnace
Used to produce niobium welded pipe
Used in the production of human implants.
Product detail pictures:
Related Product Guide:
The consumer fulfillment is our primary goal. We uphold a consistent level of professionalism, top quality, credibility and service for Cobalt Metal - Niobium Target – HSG Metal , The product will supply to all over the world, such as: Dominica, Norwegian, Thailand, We can meet the various needs of customers at home and abroad. We welcome new and old customers to come to consult & negotiate with us. Your satisfaction is our motivation! Let us work together to write a brilliant new chapter!
By Caroline from Poland - 2017.11.11 11:41
Products and services are very good, our leader is very satisfied with this procurement, it is better than we expected,
By Deirdre from Buenos Aires - 2018.12.25 12:43
Related products
-
Cobalt Metal Price - Tantalum Target – H...
Product parameters Product Name：high purity tantalum target pure tantalum target Material Tantalum Purity 99.95%min or 99.99%min Color A shiny, silvery metal that is very resistant to corrosion. Other name Ta target Standard ASTM B 708 Size Dia >10mm * thick >0.1mm Shape Planar MOQ 5pcs Delivery time 7days Used Sputtering Coating Machines Table 1: Chemical composition Chemistry (%) Designation Chief component Impurities maxmium Ta Nb Fe...
-
Chromium Metal Price - GOOD QUALITY PURE CHROM...
Metal Chromium Lump / Cr Lmup Grade Chemical Composition % Cr Fe Si Al Cu C S P ≧ ≦ HRCR99-A 99 0.30 0.25 0.30 0.01 0.01 0.01 0.01 HRCR99-B 99 0.40 0.30 0.30 0.00 0.02 0.02 0.01 HRCR98.5-A 98.5 0.45 0.35 0.50 0.04 0.03 0.02 0.01 HRCR98.5-B 98.5 0.50 0.40 0.50 0.06 0.03 0.02 0.01 HRCR98 98 0.80 0.40 0.80 0.02 0.05 0.03 0.01 Description Metal chromi...
-
Tungsten Carbide Scrap Price Per Kg - High Den...
Product Parameters Tungsten Block Polished 1kg Tungsten Cube 38.1mm Purity W≥99.95% Standard ASTM B760, GB-T 3875, ASTM B777 Surface Ground Surface, Machined surface Density 18.5 g/cm3 –19.2 g/cm3 Dimensions Common sizes：12.7*12.7*12.7mm20*20*20mm 25.4*25.4*25.4mm 38.1*38.1*38.1mm Application Ornament, decoration, Balance weight, desktop, gift, target, Military industry, and so on The characteristics 1. Laser engraving tungsten cube for 1kg 2. Melting point ...
-
Indium Ingots - High Pure 99.8% titanium grade...
Product parameters Product name Titanium target for pvd coating machine Grade Titanium (Gr1, Gr2, Gr5, Gr7,GR12) Alloy target: Ti-Al, Ti-Cr, Ti-Zr etc Origin Baoji city Shaanxi Province china Titanium content ≥99.5 (%) Impurity content <0.02 (%) Density 4.51 or 4.50 g/cm3 Standard ASTM B381; ASTM F67, ASTM F136 Size 1. Round target: Ø30–2000mm, thickness 3.0mm–300mm; 2. Plate Targe: Length: 200-500mm Width:100-230mm Thickness:3–40mm; 3. Tube target: Dia...
-
Moly Bar - Niobium Target – HSG Metal
Product parameters Specification Item ASTM B393 9995 pure polished niobium target for industry Standard ASTM B393 Density 8.57g/cm3 Purity ≥99.95% Size according to customer’s drawings Inspection Chemical composition testing, Mechanical testing, Ultrasonic inspection, Appearance size detection Grade R04200, R04210, R04251, R04261 Surface polishing, grinding Technique sintered, rolled, forged Feature High temperature resistance, corrosion resistance Application S...
-
Moly Bar - Tungsten Target – HSG Metal
Product parameters Product Name Tungsten(W)sputtering target Grade W1 Available Purity(%) 99.5%,99.8%,99.9%,99.95%,99.99% Shape: Plate, round, rotary, pipe/tube Specification As customers demands Standard ASTM B760-07,GB/T 3875-06 Density ≥19.3g/cm3 Melting point 3410°C Atomic volume 9.53 cm3/mol Temperature coefficient of resistance 0.00482 I/℃ Sublimation heat 847.8 kJ/mol(25℃) Latent heat of melting 40.13±6.67kJ/mol State Planar tungsten target,Rotating tung...