99.995 Indium Ingot - Niobium Target – HSG Metal
99.995 Indium Ingot - Niobium Target – HSG Metal Detail:
Product parameters
| Specification | |
| Item | ASTM B393 9995 pure polished niobium target for industry |
| Standard | ASTM B393 |
| Density | 8.57g/cm3 |
| Purity | ≥99.95% |
| Size | according to customer’s drawings |
| Inspection | Chemical composition testing, Mechanical testing, Ultrasonic inspection, Appearance size detection |
| Grade | R04200, R04210, R04251, R04261 |
| Surface | polishing, grinding |
| Technique | sintered, rolled, forged |
| Feature | High temperature resistance, corrosion resistance |
| Application | Superconducting industry, Aerospace aviation, Chmeical Industry, Mechanical |
|
Chemical Composition |
|||
| Grade |
R04200 |
R04210 |
|
| Main element |
Nb |
Bal |
Bal |
| Impurity elements |
Fe |
0.004 |
0.01 |
|
Si |
0.004 |
0.01 |
|
|
Ni |
0.002 |
0.005 |
|
|
W |
0.005 |
0.02 |
|
|
Mo |
0.005 |
0.01 |
|
|
Ti |
0.002 |
0.004 |
|
|
Ta |
0.005 |
0.07 |
|
|
O |
0.012 |
0.015 |
|
|
C |
0.035 |
0.005 |
|
|
H |
0.012 |
0.0015 |
|
|
N |
0.003 |
0.008 |
|
|
Mechanical Property |
|||
|
Grade |
Tensile Strength ≥ Mpa |
Yield Strength ≥ Mpa(0.2% residual deformation) |
Extend Rate % (25.4mm measurement) |
|
R04200 R04210 |
125 |
85 |
25 |
|
Content, Max, Weight % |
||||
|
Element |
Grand: R04200 |
Grand:R04210 |
Grand:R04251 |
Grand:R04261 |
|
Unalloyed Niobium |
Unalloyed Niobium |
(Reactor grade niobium-1% Zirconium) |
(Commercial grade niobium-1% Zirconium) |
|
|
C |
0.01 |
0.01 |
0.01 |
0.01 |
|
O |
0.015 |
0.025 |
0.015 |
0.025 |
|
N |
0.01 |
0.01 |
0.01 |
0.01 |
|
H |
0.0015 |
0.0015 |
0.0015 |
0.0015 |
|
Fe |
0.005 |
0.01 |
0.005 |
0.01 |
|
Mo |
0.01 |
0.02 |
0.01 |
0.05 |
|
Ta |
0.1 |
0.3 |
0.1 |
0.5 |
|
Ni |
0.005 |
0.005 |
0.005 |
0.005 |
|
Si |
0.005 |
0.005 |
0.005 |
0.005 |
|
Ti |
0.02 |
0.03 |
0.02 |
0.03 |
|
W |
0.03 |
0.05 |
0.03 |
0.05 |
|
Zr |
0.02 |
0.02 |
0.8~1.2 |
0.8~1.2 |
|
Nb |
Remainder |
Remainder |
Remainder |
Remainder |
Product technology
The vacuum electron beam melting process produces niobium plates. The unforged niobium bar is first smelted into a niobium ingot through a vacuum electron beam melting furnace. It is usually divided into single smelting and multiple smelting. We usually use twice smelted niobium ingots. Depending on the product requirements, we can perform more than two smelting.
Application
Superconducting industry
Used to produce niobium foil
Heat shield in high temperature furnace
Used to produce niobium welded pipe
Used in the production of human implants.
Product detail pictures:
Related Product Guide:
Dedicated to strict quality control and thoughtful customer service, our experienced staff members are always available to discuss your requirements and ensure full customer satisfaction for 99.995 Indium Ingot - Niobium Target – HSG Metal , The product will supply to all over the world, such as: Washington, panama, Sao Paulo, We warmly welcome your patronage and will serve our clients both at home and abroad with products of superior quality and excellent service geared to the trend of further development as always. We believe you will benefit from our professionalism soon.
By Sandy from Greek - 2018.10.09 19:07
The company comply with the contract strict, a very reputable manufacturers, worthy a long-term cooperation.
By Jonathan from Madagascar - 2018.06.28 19:27
Related products
-
PriceList for Tungsten Carbide Scrap - Customi...
Product Parameters Material tungsten Color sintered, sandblasting or polishing Purity 99.95% Tungsten Grade W1,W2,WAL,WLa,WNiFe Product Feature High melting point, High- density, high temperature oxidation resistance, long service life, resistance to corrosion. Property high hardness and strength, excellent corrosion resistance Desity 19.3/cm3 Dimension Customized Standard ASTM B760 Melting point 3410℃ Design&Size OEM or ODM acceptable Chemical Compositio...
-
High Carbon Chromium Metal Powder - GOOD QUALI...
Metal Chromium Lump / Cr Lmup Grade Chemical Composition % Cr Fe Si Al Cu C S P ≧ ≦ HRCR99-A 99 0.30 0.25 0.30 0.01 0.01 0.01 0.01 HRCR99-B 99 0.40 0.30 0.30 0.00 0.02 0.02 0.01 HRCR98.5-A 98.5 0.45 0.35 0.50 0.04 0.03 0.02 0.01 HRCR98.5-B 98.5 0.50 0.40 0.50 0.06 0.03 0.02 0.01 HRCR98 98 0.80 0.40 0.80 0.02 0.05 0.03 0.01 Description Metal chromi...
-
Ferro Molybdeen - China Ferro Molybdenum Facto...
Chemical Composition FeMo composition (%) Grade Mo Si S P C Cu FeMo70 65-75 2 0.08 0.05 0.1 0.5 FeMo60-A 60-65 1 0.08 0.04 0.1 0.5 FeMo60-B 60-65 1.5 0.1 0.05 0.1 0.5 FeMo60-C 60-65 2 0.15 0.05 0.15 1 FeMo55-A 55-60 1 0.1 0.08 0.15 0.5 FeMo55-B 55-60 1.5 0.15 0.1 0.2 0.5 Products Description Ferro Molybdenum70 is mainly used to add molybdenum to steel in steel making. Molybde...
-
Chromium Metal Ingots Price Ton - GOOD QUALITY...
Metal Chromium Lump / Cr Lmup Grade Chemical Composition % Cr Fe Si Al Cu C S P ≧ ≦ HRCR99-A 99 0.30 0.25 0.30 0.01 0.01 0.01 0.01 HRCR99-B 99 0.40 0.30 0.30 0.00 0.02 0.02 0.01 HRCR98.5-A 98.5 0.45 0.35 0.50 0.04 0.03 0.02 0.01 HRCR98.5-B 98.5 0.50 0.40 0.50 0.06 0.03 0.02 0.01 HRCR98 98 0.80 0.40 0.80 0.02 0.05 0.03 0.01 Description Metal chromi...
-
Ferroniobium - Niobium Target – HSG Metal
Product parameters Specification Item ASTM B393 9995 pure polished niobium target for industry Standard ASTM B393 Density 8.57g/cm3 Purity ≥99.95% Size according to customer’s drawings Inspection Chemical composition testing, Mechanical testing, Ultrasonic inspection, Appearance size detection Grade R04200, R04210, R04251, R04261 Surface polishing, grinding Technique sintered, rolled, forged Feature High temperature resistance, corrosion resistance Application S...
-
Hot New Products Iron Molybdenum - High Qualit...
Chemical Composition Mo ≥99.95% Fe <0.005% Ni <0.003% Cu <0.001% Al <0.001% Si <0.002% Ca <0.002% K <0.005% Na <0.001% Mg <0.001% Mn <0.001% W <0.015% Pb <0.0005% Bi <0.0005% Sn <0.0005% Sb <0.001% Cd <0.0005% P <0.001% S <0.002% C <0.005% O 0.03~0.2% Purpose High pure molybdenum is used as mammography, semiconductor and wiring materials, and other high-tech materials, also used in rocket nozzle, catalyst, ch...